The process is expensive because it's a very low volume product and it's a heterogenous mixture that needs to be stored and processed without separating, rather

The process is expensive because it's a very low volume product and it's a heterogenous mixture that needs to be stored and processed without separating, rather than an alloy. It has been possible to print with metal clay for a very long time, with every paste extrusion setup made so far, the major problem is material cost and firing. I don't expect an object made with metal clay to handle 5000psi in compression, but it might be possible with some clever geometry. The major issue with metal clay is that is behaves like clay in many ways, severely limiting geometry that can be fired without breaking. You can think of it as very high viscosity solder paste.