Why would a tungsten band increase the chances of degloving your finger? A tungsten band is a lot harder than a gold band. But a gold band is already way harde
by dpark 11d ago
Why would a tungsten band increase the chances of degloving your finger?
A tungsten band is a lot harder than a gold band. But a gold band is already way harder than your flesh. Jimmy Fallon was wearing a traditional platinum band when he nearly lost his finger.
If you want to reduce your risk, you should either not wear a ring or wear a silicone band.
- kenniskrag 11d agoIn a hospital, they may need to remove the ring quickly for example, if your finger was injured and begins to swell.
- happyopossum 11d agoIn a hospital setting nobody will be degloving your finger - this is a common situation, and they have pliers that will crack/shatter the tungsten for removal.
- phyzome 11d agoI'm guessing that strongly depends on how big the hospital is. I know someone who lives out in the boonies and it's amazing what isn't on hand.
- Ancapistani 10d agoI live in a town of <15k people, and it’s the county seat. Our hospital can handle tungsten carbide rings without issue. I checked before getting one for this very reason (though I now wear an Oura as my wedding ring).
- bluGill 11d agoSteel toed work boots are almost never allowed to have a steel toe anymore. It is always plastic which is just as strong but it shatters when it breaks so they don't have to uncrush that once they get whatever fell on your toes off. There are some rare exceptions for specific jobs, see OSHA (or your country equivalent) for the exact rules that apply to you.
- Clent 11d agoThis isn't remotely true. Steel is absolutely still allowed. The steel toe is designed to collapse without crushing the toe. When that happens, the boot needs to be replaced. There are composites which are fiber based but those aren't labelled as steel toes, they aren't designed to shatter and it's not plastic.
- bluGill 11d agoOsha allows steel where plastic (fiber is a plastic) has issues. However they have complex rules and none of the industries I work with will allow steel.
- tredre3 11d agoI've been wearing them all my life all over North America. Very few industries require metal-free footwear. Composite toes (since we're getting carried away with various terms, that's the actual term and fabrication method, which is fiber mesh and epoxy) still have downsides. Those don't apply if you're a white collar guy and just need them because of regulations. But if you're an actual worker that relies on them to save your toes, CT has much worse puncture resistance than ST. So it's trivial to puncture with a framing nail gun or cut through it if you rest a board on your toe, for example. They also shatter when something heavy falls on them. If the thing bounces and you're quick enough to pull your foot, then great. If not, the second bounce will be shattering your toes and your boot will be filled with fleshy composite soup that is impossible to save. A steel toe in that situation will just bend and odds are good that your foot will be salvageable.
- dpark 11d agoTungsten also shatters. It doesn’t crush. That’s actually how a tungsten ring that’s stuck is removed. You break it with a vice.
- monster_truck 9d agoGo check out the OSHA injury reports my dude. All it takes is something like a seemingly harmless hop over a short chain fence gone wrong. Where any other band would deform or break, that fucker's taking everything else with it.
- dpark 9d agoMy dude the question is not what danger a ring poses but why tungsten poses a higher risk. The flesh on your finger is much softer than a normal wedding band. Again, Jimmy Fallon is an excellent example of this. He fell in his kitchen and his very traditional platinum band took the flesh off his finger when it caught on the counter.