That's not actually true though. I find SAC305 to wick into joints faster than leaded solder does, provided you have quality flux in the solder. If you get th
by CarVac 3y ago
That's not actually true though.
I find SAC305 to wick into joints faster than leaded solder does, provided you have quality flux in the solder.
If you get the cheapest lead-free solder you can find on Amazon it will be bad.
Doubly so if you have a non-temperature-controlled soldering iron. Too cold, and it won't melt effectively. Too hot, and exposed metal will oxidize rapidly.
- djmips 3y agoWhat is your favoured temperature for let's say through hole DIP connections?
- CarVac 3y ago650°F or 340°C. Works beautifully with SAC305.
- tpmx 3y agoprovided you have quality flux in the solder which you often don't need with leaded solder.
- CarVac 3y agoYes, you need slightly better flux to avoid using toxic heavy metal in your hobby electronics.