I can see why that would be useful in some circumstances, but not the more common ones they describe. Why is it necessary that a ceramic heatsink for a phone be
by Mizza 4y ago
I can see why that would be useful in some circumstances, but not the more common ones they describe. Why is it necessary that a ceramic heatsink for a phone be re-formed, rather than just cast in the correct shape to begin with?
- ccvannorman 4y agoI'm not sure, but here's what might be the case: If you have a phone made of today's ceramics and drop in on concrete, and it cannot be deformed, it will shatter. Since this new material can be malleable, when you drop your phone, it doesn't shatter.
- Mizza 4y agoThat would be handy, but that's not the case here since it only deforms under high heat/pressure, not in normal room temperature conditions.
- quells 4y agoIt’s incredibly difficult to form conventional ceramics into “the correct shape to begin with” with even millimeter tolerances because it shrinks twice during production. First when the liquid from the slurry/clay evaporates, and again when the particles sinter together during firing in the kiln. Both of these are non-linear and can cause warping with complex geometries. EDIT: binders also typically burn off during firing, which further complicates changing shape during firing.
- hinkley 4y agoIt’s kind of amazing that you can get a ceramic container where the lid fits snuggly. Some of that comes from modifying the greenware (dried but unfired clay) but I think most of it is exacting tolerances for inputs and processing. Clay from this one quarry. This much water. These building temperatures and humidity. This exact furnace temperature and time.
- ruste 4y agoThe only way I've seen this done is by lapping the touching surfaces after firing.
- amluto 4y agoOne can fire a pot with the lid on it in the kiln. They tend to deform together. Of course, this requires that the mating surfaces not fuse together and may also produce a non-rotationally-symmetric interface.
- hinkley 4y agoI feel like I've watched videos where people make Japanese and/or Korean ceramic cook pots and I can't for the life of me remember how they kept them from warping, just that they do. The only trick I do remember is don't glaze the contact point between the two pieces. That not only adds thickness variability, but if glaze touches the bottom of the kiln you fuse to the bricks, so you have to elevate anything glazed, and elevating increases warping.
- creeble 4y agoHow do they create things like ceramic turbo turbines and ceramic exhaust manifolds? Seems like the shrinkage problem would prevent these close tolerances.
- lazide 4y agoLots of trial and error and tossed parts during manufacture. Neither of those parts are known for being cheap.
- adrian_b 4y agoThe same shrinkage problem exists for the ceramic tooth crowns. The vendor of the dental ceramic provides a program that uses a mathematical model of the shrinkage to compute the form required for the ceramic crown before sintering. Of course the mathematical model is not perfect so the dentist may still have to do some small adjustments to the sintered crown.
- hinkley 4y agoAn oven doesn’t reach 300°C, blacksmiths work metal above 800°C, when it becomes ductile. Most of us don’t seem to have problems with that notion, except when discussing 9/11 that is. If your computer is hitting oven temperatures you have a very big problem.